dc.contributor.advisorCruz, Robinson Carlos Dudley
dc.contributor.authorEcheverrigaray, Sérgio Graniero
dc.contributor.otherSalomão, Rafael
dc.contributor.otherOviedo, Mauro Alfredo Soto
dc.contributor.otherPerottoni, Cláudio Antônio
dc.contributor.otherGiacomelli, Cristiano
dc.date.accessioned2015-10-06T16:44:04Z
dc.date.available2015-10-06T16:44:04Z
dc.date.issued2015-10-06
dc.date.submitted2009-06-22
dc.identifier.urihttps://repositorio.ucs.br/handle/11338/1028
dc.descriptionOs modos de interação de silsesquioxano poliédrico oligomérico (POSS) de gaiolas fechadas com distintos grupos funcionais foram avaliados na nanoestruturação de polipropileno isotático (iPP) via processamento reativo. Analisaram-se POSS com grupos substituintes isobutila, alila e vinila em concentrações de 0,5, 1, 2 e 5%m misturados a iPP fundido utilizando peróxido de dicumila (DCP) como iniciador. Na caracterização dos nanocompósitos foram utilizadas diversas técnicas. A morfologia foi avaliada através de cromatografia por exclusão de tamanho, espectroscopia de infravermelho com transformada de Fourier, microscopia de transmissão e difração de raios X. O comportamento viscoelástico dos materiais no estado fundido foi medido por reologia oscilatória e no estado sólido por análises dinâmico-mecânicas. As transições térmicas foram levantadas tanto por análises dinâmico-mecânicas como por calorimetria diferencial de varredura. Modificações morfológicas e viscoelásticas importantes foram observadas para os nanocompósitos em dependência do tipo e teor de POSS empregado. A adição do Octaisobutil-POSS (OI) sugere ação estabilizante radicalar e lubrificante para este POSS. Os efeitos da incorporação do Alilisobutil-POSS (AL) indicam que este atuou como agente plastificante em função da concentração. Com Octavinil-POSS (OV) os nanocompósitos parecem adquirir estrutura ramificada ou interligada em dependência da concentração. A ativação radicalar promovida pelo DCP mostrou-se fundamental na enxertia de alguns POSS. Assim, a forma e intensidade das interações entre nanocargas e matriz foram definidas pelos grupos funcionais e concentração dos POSS. Alterações observadas na morfologia, propriedades térmicas e viscoelásticas são resultantes dessas formas e graus de interação. Deste modo, foi possível propor mecanismos de interação e arranjos morfológicos entre iPP, DCP e POSS pela avaliação do conjunto de resultados obtidos.pt_BR
dc.description.abstractThe interaction modes of polyhedral oligomeric silsesquioxane (POSS) of closed cages with distinct functional groups were evaluated on isotactic polypropylene (iPP) nanostructuration via reactive processing. POSS were analyzed with isobutyl, allyl and vinyl substituent groups in concentrations of 0.5, 1, 2 and 5m% mixed with melting iPP using dicumil peroxide (DCP) as initializer. Several techniques were used to characterize the nanocomposites. The morphology was evaluated through size exclusion chromatography, Fourier transformed infrared spectroscopy, transmission electron microscopy and X-ray diffraction. The samples viscoelastic behavior in melting state was measured by oscillatory rheometry and in solid state by dynamic mechanical analysis. The thermal transitions were obtained through dynamic mechanical analysis and differential scanning calorimetry. Important morphology and viscoelastic modifications were observed in nanocomposites by dependency on the type and content of POSS used. The addition of OctaIsobutyl-POSS (OI) suggests lubricant and radicalar stabilizing action for this POSS. The AllylIsobutyl-POSS (AL) incorporation effects indicate that this one acted as plasticizing agent in function of concentration. With OctaVinyl-POSS (OV), the nanocomposites seem to acquire ramified or interlinked structure in dependency on concentration. The radicalar activation promoted by DCP was decisive in the grafting efficiency for some POSS. Therefore, the mode and the interaction intensity between nanoparticles and polymeric matrix were defined by functional groups and POSS concentration. Changes observed in morphology, thermal and viscoelastic properties as in solid state as in melting state are results of these modes and interaction degrees. It was possible to propose interaction mechanisms and morphology arrangements among iPP, DCP and POSS by evaluation of the obtained results as a whole.pt_BR
dc.language.isoptpt_BR
dc.subjectNanocompósitos (Materiais)pt_BR
dc.subjectSilsesquioxano poliédrico oligoméricopt_BR
dc.subjectPolímerospt_BR
dc.subjectViscoelasticidadept_BR
dc.subjectMateriais - Testespt_BR
dc.subjectNanocomposites (Materials)pt_BR
dc.subjectPolyhedral oligomeric silsesquioxanept_BR
dc.subjectPolymerspt_BR
dc.subjectViscoelasticitypt_BR
dc.subjectMaterials - Testingpt_BR
dc.titleProcessamento reativo de nanocompósitos iPP-POSSpt_BR
dc.typeDissertationpt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/8057434446805884pt_BR
mtd2-br.author.lattesECHEVERRIGARAY, S. G.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação em Engenharia e Ciência dos Materiaispt_BR