dc.descriptionNessa dissertação foi estudada a síntese de elastômeros microcelulares de poliuretano (EMPU). Foram preparados três EMPU baseados em diisocianato de 4,4 difenilmetano (MDI), com diferentes concentrações de fase rígida (Formulações 1, 2 e 3, com 32, 35 e 42% de fase rígida, respectivamente). As amostras foram preparadas através do método de duas etapas, pelo sistema de pré-polímero. As amostras dos EMPU foram caracterizadas através de ensaios físicos, mecânicos, morfológicos, térmicos e químicos. Os resultados dos ensaios mecânicos mostraram que o aumento no percentual de fase rígida levou a um aumento na resistência à tração e na resistência ao rasgamento. O alongamento na ruptura não apresentou variação significativa com a modificação do percentual de fase rígida. As análises morfológicas indicaram que o aumento no percentual de fase rígida promoveu a formação de microcélulas menores, distribuídas de forma mais homogênea no elastômero. As análises de termogravimetria indicaram a presença de dois estágios de degradação, referentes às fases rígida e flexível, respectivamente. Os ensaios de calorimetria exploratória diferencial indicaram que os EMPU apresentam uma separação de fases à temperatura ambiente. O aumento na quantidade de fase rígida presente nos EMPU implicou em maiores valores de densidade de ligações cruzadas. O ensaio de resistência química demonstrou que os EMPU formulados apresentaram baixos índices de inchamento para solventes industriais comumente utilizados.pt_BR
dc.description.abstractIn this work, three different microcellular polyurethanes elastomers (EMPU) based on 4,4-diphenylmethane diisocyanate (MDI) with different rigid phase contents were prepared (Formulations 1, 2 and 3 with 32, 35 and 42% of rigid phase content, respectively). The EMPU were obtained by two steps method. The samples were evaluated with respect to physical, mechanical, morphological, thermal and chemical properties. The results showed that the formulation with higher rigid phase content has higher tensile and tear strength. The deformation at rupture not show significant variation with the change in the rigid phase content. Micrographs of SEM indicated that the higher rigid phase content promoted the best cells homogeneity in the samples. The termogravimetric analysis show the presence of the two degradation steps associated to the rigid and flexible phase, respectively. Diferential scanning calorimetry indicated that the EMPU has a phase separation at room temperature. The increase in the rigid phase content implicated in the increase of the cross-linked density of the material. Finally, the EMPU have good chemical resistence in comumm solvents.pt_BR
dc.language.isoptpt_BR
dc.subjectPolímeros e colóidespt_BR
dc.subjectElastômerospt_BR
dc.subjectMicrocelularpt_BR
dc.subjectPoliuretanopt_BR
dc.subjectElastomersen
dc.subjectMicrocellularen
dc.subjectPolyurethanesen
dc.titleSíntese e Caracterização de elastômeros microcelulares de poliuretanopt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/6535050564941144pt_BR
mtd2-br.author.lattesPACHECO, Marcos Fernando Molonpt_BR
mtd2-br.program.namePrograma de Pós-Graduação de Mestrado em Materiaispt_BR


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record