dc.descriptionEspumas de EVA são uma classe de materiais que combinam propriedades mecânicas com densidade reduzida, além da capacidade de absorção de energia e impacto, e por isso são amplamente aplicadas na indústria calçadista. Contudo, durante a sua fabricação e uso para confecção de calçados muitas aparas acabam tornando-se resíduo. Nesse sentido, o presente estudo tem como objetivo um processo de reciclagem, de forma a incorporar as aparas na fabricação de novas espumas. Inicialmente, os resíduos das espumas foram submetidos a um processo de extrusão duplarrosca, com a alteração de diferentes parâmetros de processamento, tais como o número de reprocessamentos, a temperatura, a velocidade de rotação e o uso de antioxidante. Nessa primeira etapa foram avaliadas as características do reciclado através dos ensaios de teor de gel, microscopia eletrônica de varredura (MEV), termogravimetria (TG) e reometria de placas paralelas e de torque. A partir disso, foram escolhidas as quatro amostras, das dezesseis extrusadas, com maior probabilidade de formar espumas homogêneas. Então seguiu-se com a confecção de espumas de EVA com e sem a incorporação do reciclado, e foram avaliados os seguintes parâmetros das espumas desenvolvidas: microscopia eletrônica de varredura (MEV), análise dinâmico mecânico (DMA) e ensaios físicos de densidade, abrasão e deformação permanente por compressão (DCP). Os resultados demonstraram uma diminuição do teor de gel reticulado em até 13 pontos percentuais para a amostra processada com antioxidante no quinto reprocessamento. Assim como as menores viscosidades para essas mesmas amostras em relação ao processamento anterior. Contudo, ocorreu uma possível reticulação residual, pois a viscosidade de todas as amostras é maior do que referência (espuma). A maior homogeneidade, observada no MEV, ocorreu nas amostras processadas por cinco repetições sem antioxidante. Esses parâmetros permitiram a escolha do reciclado para a confecção das espumas. Algumas amostras apresentaram aspectos muito semelhantes à espuma de EVA confeccionada sem reciclado. A partir do MEV pode-se perceber a espuma com reciclado extrusado uma vez, a 180°C, 450 rpm, sem antioxidante (amostra G1), como a mais uniforme e de células esféricas. Essa espuma também apresentou as melhores respostas para os ensaios de físicos de DCP e abrasão, inclusive comparada à espuma sem reciclado.pt_BR
dc.description.abstractEVA foam is a class of materials that combine mechanical properties with reduced density and the ability to absorb energy and impact, which is why they are widely applied in the footwear industry. However, during its manufacture and use, many shavings scraps end up becoming waste. In this sense, the present study aims to develop a recycling process, in order to be able to incorporate the EVA waste in the manufacture of new foams. Initially, the foam waste was processed in a twin screw extruder, with the alteration of different processing parameters, such as the number of reprocessing, temperature, rotation speed and the use of antioxidants. In this first stage, the characteristics of the recycled were evaluated through the gel content tests, scanning electron microscopy (SEM), thermogravimetry (TG) and parallel and torque plate rheometry. From the sixteen samples extruded, four samples with the highest probability of forming homogeneous foams were chosen. Then, EVA foams were made with and without the incorporation of recycled material, and the following parameters of the new foams were evaluated: scanning electron microscopy (SEM), dynamic mechanical analysis (DMA) and physical density, abrasion tests and permanent compression deformation (PCD). The results demonstrated a decrease in the content of crosslinked gel by up to 13 percentage points for the sample processed with antioxidant. As well as the lower viscosities for these same samples. However, there was a possible residual crosslinking, as the viscosity of all samples is greater than the reference (foam). The greatest homogeneity, observed in the SEM, occurred in the samples processed for five repetitions without antioxidant. These parameters allowed to choose the recycled material for making new foams. Some of them presented very similar aspects to EVA foam made without recycled content. From the SEM you can see the foam with recycled extruded once, at 180 °C, 450 rpm, without antioxidant (sample G1), as the most uniform and spherical cells. This foam also showed the best responses for the physical tests of DCP and abrasion, even compared to foam without recycled content.en
dc.description.sponsorshipConselho Nacional de Desenvolvimento Científico e Tecnológico, CNPqpt_BR
dc.language.isoptpt_BR
dc.subjectResíduos industriaispt_BR
dc.subjectProdutos recicladospt_BR
dc.subjectAcetato de vinilapt_BR
dc.subjectFactory and trade wasteen
dc.subjectRecycled productsen
dc.subjectVinyl acetateen
dc.titleAvaliação da utilização de agente antioxidante na reciclagem de resíduos de etileno-acetato de vinila (EVA) reticuladopt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/3594976734800450pt_BR
mtd2-br.author.lattesROSA, V. B.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação em Engenharia de Processos e Tecnologiaspt_BR
mtd2-br.contributor.coorientadorZattera, Ademir José


Files in questo item

Thumbnail
Thumbnail

Questo item appare nelle seguenti collezioni

Mostra i principali dati dell'item