dc.descriptionPara que seja possível explorar ao máximo o potencial dos nanocompósitos é preciso que haja interação entre o reforço e a matriz. Este trabalho estuda a ação dos ácidos hexanóico (C6), octanóico (C8) e decanóico (C10) como agentes de acoplamento em compósitos de polipropileno (PP) reforçados com óxido de grafeno (OG). Foram preparadas amostras de PP, PP/OG, PP/OG/C6, PP/OG/C8 e PP/OG/C10 em um misturador termocinético e em seguida moldadas por compressão. Foram avaliadas suas morfologias por microscopia eletrônica de varredura; suas propriedades mecânicas através de ensaios de resistência à flexão e resistência ao impacto; e sua estabilidade térmica por análise termogravimétrica. As amostras PP/OG/C8 e PP/OG/C10, frente à amostra de PP/OG, apresentaram resultados inferiores, na ordem de 15 a 40%, em todos os ensaios mecânicos, com exceção do ensaio de módulo de flexão, em que a amostra PP/OG/C8 apresentou um resultado cerca de 6% superior. Essas mesmas amostras pouco diferiram do PP/OG nas análises termogravimétricas. A amostra PP/OG/C6, entretanto, apresentou resultados muito próximos para deformação e resistência à flexão, resultado 10% superior para o módulo de flexão e 39% superior para resistência ao impacto frente ao PP/OG. Além disso, a amostra PP/OG/C6 apresentou maior estabilidade térmica, tendo uma temperatura de 3% de perda de massa 17% superior que a do PP/OG. Com base nisso constatou-se que o ácido hexanóico é o que apresenta melhor ação compatibilizante entre os três compostos avaliados. [resumo fornecido pelo autor]pt_BR
dc.description.abstractTo fully explore the potencial of nanocomposites, it is necessary interaction between filler and matrix. This study evaluates the coupling action of the hexanoic (C6), octanoic (C8) and decanoic (C10) acids in polypropylene (PP)/graphene oxide (GO) nanocomposites. Samples of neat PP, PP/OG, PP/OG/C6, PP/OG/C8, PP/OG/C10 were prepared in a thermokinetic mixer followed by compression molding. The morphology was evaluated by scanning electron microscopy; the mechanical properties through the flexural strength and impact resistance tests; and the thermal stability by thermogravimetric analysis. The PP/OG/C8 and PP/OG/C10 samples, compared to the PP/OG sample, had inferior results, around 15 to 40%, in all mechanical tests, with the exception of the flexural strenght, in wich the PP/OG/C8 sample had a result around 6% higher. These same two samples differ too little from the PP/OG sample in the thermogravimetric analisis. The PP/OG/C6 sample, however, had very similar results in deformation and flexural resistance, a result 10% higher for flexural modulus and 39% higher for impact resistance when compared to PP/OG. Furthermore, the PP/OG/C6 sample showed greater thermal stability, having a temperature of 3% mass loss 17% higher than PP/OG. Based on these results it was concluded that the hexanoic acid shows the greatest coupling action among the three evaluated compounds. [resumo fornecido pelo autor]pt_BR
dc.language.isoptpt_BR
dc.subjectNanocompósitos (Materiais)pt_BR
dc.subjectPolipropilenopt_BR
dc.subjectÓxidospt_BR
dc.subjectEngenharia químicapt_BR
dc.titleAvaliação da ação compatibilizante dos ácidos hexanóico, octanóico e decanóico em compósitos de polipropileno reforçados com óxido de grafenopt_BR
dc.typeMonografiapt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.program.nameBacharelado em Engenharia Químicapt_BR
mtd2-br.campusCampus Universitário de Caxias do Sulpt_BR
local.data.embargo2021-12-13


Dateien zu dieser Ressource

Thumbnail

Das Dokument erscheint in:

Zur Kurzanzeige