dc.descriptionOs postes de madeira da rede de distribuição de energia elétrica são tratados com preservantes para aumentar sua vida útil. Dentre os diversos tipos de preservantes de madeira disponíveis no mercado, o mais utilizado é o arseniato de cobre cromatado (CCA), tendo em vista a sua elevada eficiência para preservar a madeira. A presença de metais nestes preservantes exige uma destinação adequada ao fim da vida útil do poste. O presente estudo propõe a utilização do processo de pirólise como uma alternativa para a destinação final dos postes de madeira removidos da rede de distribuição de energia elétrica. A pirólise da madeira tratada com CCA promove a liberação de compostos voláteis perigosos devido à presença dos metais (Cr/Cu/As) em sua composição. Com o intuito de minimizar estas emissões, reagentes de baixo custo (a base de cálcio) podem ser utilizados durante o processo pirolítico. Neste trabalho, foram avaliados os efeitos de diferentes parâmetros de operação (temperatura, tempo de isoterma, taxa de aquecimento, razão madeira/CaO e velocidade superficial) sobre a retenção dos metais no char da madeira tratada com CCA, bem como a influência dos compostos de cálcio sobre o poder calorífico do gás combustível gerado no processo de pirólise. A caracterização da madeira tratada com CCA indicou diferenças na composição química das frações testadas (C1-alburno externo, C2-alburno interno e C3-cerne), especialmente no teor de metais. As análises para a determinação da distribuição de metais indicaram que a concentração de compostos metálicos tende à zero na linha central do poste, de forma que a elevada concentração de metais está localizada na fração externa do poste. Na análise imediata, foi observado um teor mais elevado de cinzas na fração externa da madeira. Na Espectroscopia no Infravermelho com Transformada de Fourier (FTIR) a madeira com CCA apresentou bandas similares a de uma biomassa convencional. Na Análise Termogravimétrica (TGA), observaram-se picos próximos a 276 e 354 ºC, referentes à degradação térmica das hemiceluloses e da celulose, respectivamente. A energia de ativação determinada pelo método de Kissinger foi próxima a 156 kJ·mol-1. A Ea média calculada no método de Flynn-Wall-Ozama foi de aproximadamente 153 kJ·mol-1 para C1, 182 kJ·mol-1 para C2 e 170 kJ·mol-1 para C3. Os mecanismos de reação no estado sólido verificados no método de Criado foram comandados, em sua maioria, por processos de difusão. Sob condições controladas de operação, (temperatura, tempo de residência e vazão de ar) o carbonato de cálcio (CaCO3) foi calcinado visando a obtenção de óxido de cálcio (CaO) com elevada área superficial. Os ensaios preliminares de calcinação indicaram que o CaO com maior área superficial foi obtido a 850 ºC com um tempo de residência de 5 min. Na primeira série de ensaios de pirólise verificou-se que à medida que CaO foi adicionado ao sistema, a emissão de metais e a produção de óleo foram inferiores. No segundo lote dos ensaios de pirólise, os efeitos preponderantes para a retenção dos metais no char foram a granulometria elevada das partículas, a adição de CaO e a taxa de aquecimento. Devido à adição de CaO, obteve-se menor concentração de CO2 e foi produzido um gás combustível com poder calorífico próximo a 25 MJ·Nm-3.pt_BR
dc.description.abstractWooden poles of the electricity distribution network are treated with preservatives to increase their shelf life. Among the various types of wood preservatives available on the market, the most used is the chromated copper arsenate (CCA), due to its high efficiency for preserving wood. The presence of metals in these preservatives requires proper disposal at the end of pole life. This study proposes the use of pyrolysis process (under controlled conditions) as an alternative to wooden poles disposal after removed from the electricity distribution network. The pyrolysis of CCA treated wood promotes the release of dangerous volatile compounds due to the presence of metals (Cr/Cu/As) in its composition. In order to minimize these emissions, low cost reagents (based on calcium) can be used during the pyrolytic process. In this work, the effect of different operating parameters (temperature, residence time, heating rate, wood/CaO ratio and superficial velocity) on the retention of metals in the char was evaluated, as well as the influence of calcium compounds on the calorific value of the fuel gas generated in the pyrolysis process. The characterization of CCA treated wood indicated differences in the chemical composition of the tested fractions (C1-sapwood, C2- outer core and C3-cord), especially in the metal content. The metals distribution analysis indicated that the concentration of metallic compounds tend to zero at the center of the pole, so the high concentration of metal is located on the outer portion. In the proximate analysis, a higher ash content on the outer portion was observed. Fourier Transform Infrared Spectroscopy (FTIR) showed bands very similar to a conventional biomass. In Thermogravimetric Analysis (TGA) peaks centered at 276 and 354 ºC were observed, relating to thermal degradation of hemicellulose and cellulose respectively. The activation energy determined by the Kissinger method was approximately 156 kJ·mol-1. The mean activation energy by the Flynn-Wall-Ozama method was 153 kJ·mol-1 for C1, 182 kJ·mol-1 for C2 and 170 kJ·mol-1 for C3. The degradation reaction mechanism determined by using the Criado is mostly controlled by diffusion processes. Under controlled operating conditions (temperature, residence time and air flow) calcium carbonate (CaCO3) was heated in order to obtain calcium oxide (CaO) with a higher surface area. Preliminary tests indicated that the calcination of CaO with greater surface area was obtained at 850 ºC with a residence time of 5 min. In the first series of pyrolysis tests, as CaO was added to the system, lesser metals emission and oil yield were observed. In the second set of pyrolysis tests, the relevant effects identified on the retention of metals was the high particle size of the wood, the addition of CaO and the heating rate. Due to the addition of CaO, the CO2 concentration was reduced and it was produced a combustible gas with a calorific value close to 25 MJ·Nm-3.en
dc.description.sponsorshipCompanhia Paulista de Força e Luz, CPFLpt_BR
dc.language.isoptpt_BR
dc.subjectMadeirapt_BR
dc.subjectPirólisept_BR
dc.subjectCalpt_BR
dc.subjectWooden
dc.subjectPyrolysisen
dc.subjectLimeen
dc.titlePirólise de madeira tratada com CCA em reator de leito fixopt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/1274987561288217pt_BR
mtd2-br.author.lattesJUNGES, J.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação em Engenharia de Processos e Tecnologiaspt_BR
mtd2-br.contributor.coorientadorDettmer, Aline


Arquivos deste item

Thumbnail

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples