| dc.description | O objetivo deste estudo foi avaliar a contração em produtos poliméricos injetados, e os efeitos do processo que alteram este valor. Através de um molde já existente, foram realizadas simulações de injeção em software para encontrar os parâmetros a serem reproduzidos na máquina injetora durante os ensaios. Para a validação destes parâmetros, foi utilizado um termopar que mediu a temperatura interna do molde, garantindo a similaridade entre os dados teóricos extraídos da simulação computacional e os resultados do ensaio em máquina. Após as amostras necessárias serem produzidas, foram realizadas as análises metrológicas e criado uma base de dados para comparação das deformações da peça física, com a deformação que o software de simulação indicou. Foram avaliados parâmetros como a repetibilidade do processo e a confiabilidade da simulação para definir um valor médio de contração em cada caso. Os resultados da simulação de injeção indicaram percentuais de contração de 1,29 % para a menor pressão de injeção utilizada (22 bar) e 0,75 % para a maior (190 bar). Nos testes práticos, os valores variaram de 0,58% até 0,69% para 19 bar e 190 bar respectivamente. [resumo fornecido pelo autor] | pt_BR |
| dc.description.abstract | The aim of this study was to evaluate the shrinkage in injected polymeric products, and the process effects that change this value. Through an existing mold, injection simulations were carried out in software to find the parameters to be reproduced in the injection machine during the tests. For the validation of these parameters, a thermocouple was used that measured the internal temperature of the mold, ensuring the similarity between the theoretical data extracted from the computer simulation and the results of the machine test. After the necessary samples were produced, metrological analyzes were performed and a database was created to compare the deformations of the physical part, with the deformation that the simulation software indicated. Parameters such as process repeatability and simulation reliability were evaluated to define an average shrinkage value in each case. The results of the injection simulation indicated contraction percentages of 1,29% for the lowest injection pressure used (22 bar) and 0,75% for the highest one (190 bar). For the tests, the values ranged from 0,58% to 0,69% for 19 bar and 190 bar respectively. [resumo fornecido pelo autor] | pt_BR |
| dc.language.iso | pt | pt_BR |
| dc.subject | Polímeros | pt_BR |
| dc.subject | Engenharia mecânica | pt_BR |
| dc.title | Estudo da contração de produtos poliméricos injetados | pt_BR |
| dc.type | Monografia | pt_BR |
| mtd2-br.advisor.instituation | Universidade de Caxias do Sul | pt_BR |
| mtd2-br.program.name | Bacharelado em Engenharia Mecânica | pt_BR |
| mtd2-br.campus | Campus Universitário de Caxias do Sul | pt_BR |
| local.data.embargo | 2022-07-25 | |