dc.descriptionA cicatrização de feridas pode ser retardada em função da resistência e da tolerância a vários antimicrobianos tópicos que são frequentemente utilizados para essa finalidade. Nesse contexto, o desenvolvimento de curativos com materiais que possuem propriedades angiogênicas e bactericidas é desejável, uma vez que possibilitam tratar tais infecções por um longo período de tempo e de forma local. Nesse estudo foram preparados filmes de látex de borracha natural (LBN) contendo própolis vermelha e óxido de cobre (II)/nanopartículas de óxido de cobre (II) (CuO/CuONPs). Os filmes foram obtidos em diferentes condições de temperatura e tempo (65 ºC por 24 h, 40 ºC por 24 h, 40 ºC por 12 h com circulação forçada de ar, e à temperatura ambiente). Tratamentos superficiais adicionais com plasma, utilizando os gases oxigênio, hidrogênio e uma mistura de ambos, além da deposição de cobre usando a técnica de magnetron sputtering, foram igualmente realizados. Os filmes foram então caracterizados pelas técnicas de espectroscopia no infravermelho com transformada de Fourier e refletância total atenuada (FTIR-ATR), microscopia eletrônica de varredura com emissão de campo (MEV-FEG), espectroscopia por dispersão em energia (EDS) e fluorescência de raios X (XRF), e por medidas de ângulo de contato. A liberação de cobre dos filmes, por sua vez, foi avaliada pela técnica de espectroscopia de emissão atômica por plasma acoplado indutivamente (ICP-OES), enquanto os ensaios antibacterianos foram realizados com inóculos de Escherichia coli. De modo geral, os filmes apresentaram caráter hidrofílico, com valores de ângulo de contato entre 22º e 65º; porém, com o passar do tempo, e devido ao envelhecimento do LBN, tornam-se mais hidrofóbicos. Além disso, os resultados obtidos a partir dos filmes que foram preparados por meio da incorporação direta de CuO/CuONPs ao látex indicaram ausência de atividade bactericida, uma vez que o cobre reage com a matriz polimérica, promovendo a desintegração dos mesmos com o passar do tempo e, consequentemente, impossibilitando a visualização do mesmo por MEV-FEG e EDS. Em contrapartida, os resultados inerentes aos filmes preparados por magnetron sputtering revelaram que o modo de acondicionamento influencia diretamente na atividade bactericida. Os filmes conservados em dessecador apresentaram propriedades bacteriostáticas a partir de 10 s de deposição de cobre, enquanto aqueles que ficaram sob a bancada apresentaram uma menor atividade bacteriostáticas, devido à formação de óxidos. A análise por meio das técnicas de MEV-FEG e EDS demonstrou que a quantidade de cobre na superfície das amostras e o aumento do ângulo de contato estão diretamente ligados ao tempo de deposição de cobre. O resultado de liberação de cobre foi 0,16 mg/L, estando bem abaixo do limite padrão para lançamento de efluentes. Finalmente, o conjunto de todos os resultados indicou que os filmes de LBN/própolis vermelha/cobre podem ser considerados uma alternativa frente aos curativos de feridas tradicionais; porém, estudos mais aprofundados principalmente de caráter biológico, como de citotoxicidade, e a melhora da hidrofilicidade dos filmes são ainda necessários. [resumo fornecido pelo autor]pt_BR
dc.description.abstractWound healing can be delayed due to resistance and tolerance to several topical antimicrobials that are often used for this purpose. In this context, the development of dressings with materials that have angiogenic and bactericidal properties is desirable, since they make it possible to treat such infections for a long period of time and locally. In this study, natural rubber latex (NRL) films containing red propolis and copper (II) oxide/copper (II) oxide nanoparticles (CuO/CuONPs) were prepared. The films were obtained under different conditions of temperature and time (65 ºC for 24 h, 40 ºC for 24 h, 40 ºC for 12 h with forced air circulation, and at room temperature). Additional surface treatments with plasma, using oxygen, hydrogen and a mixture of both gases, in addition to copper deposition using the magnetron sputtering technique, were also performed. The films were then characterized by the techniques of infrared spectroscopy with Fourier transform and attenuated total reflectance (FTIR-ATR), scanning electron microscopy with field emission (FEG-SEM), energy dispersion spectroscopy (EDS) and X-ray fluorescence (XRF), and by contact angle measurements. The release of copper from the films was evaluated using the inductively coupled plasma optical emission spectrometry (ICP-OES) technique, while antibacterial assays were performed with inoculum of Escherichia coli. In general, the films showed a hydrophilic character, with contact angle values between 22º and 65º; however, in the course of time and due to the aging of the NRL, they become more hydrophobic. In addition, the results obtained from the films that were prepared through the direct incorporation of CuO/CuONPs into the latex indicated the absence of bactericidal activity, since copper reacts with the polymeric matrix, promoting their disintegration over time and, consequently, making it impossible to visualize it by FEG-SEM and EDS. On the other hand, the results inherent to the films prepared by magnetron sputtering revealed that the way of conditioning directly influences the bactericidal activity. The films preserved in a desiccator showed bacteriostatic properties after 10 s of copper deposition, while those that remained under the bench showed less bacteriostatic activity due to the formation of oxides. The analysis using FEG-SEM and EDS techniques demonstrated that the amount of copper on the surface of the samples and the increase in the contact angle are directly linked to the time of copper deposition. The copper release result was 0.16 mg/L, below the standard limit for wastewater release. Finally, the set of all results indicated that NRL/red propolis/copper films can be considered an alternative to traditional wound dressings; however, deeper studies, mainly of a biological nature, such as cytotoxicity and the improvement of the hydrophilicity of the films are still necessary. [resumo fornecido pelo autor]en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior, CAPESpt_BR
dc.language.isoenpt_BR
dc.language.isoptpt_BR
dc.subjectLátexpt_BR
dc.subjectMateriais biomédicospt_BR
dc.subjectPrópolept_BR
dc.titlePreparação e caracterização de filmes de látex de borracha natural contendo própolis vermelha e cobre para aplicações biomédicaspt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/7575373174502396pt_BR
mtd2-br.author.lattesBystronski, Andressa Rochapt_BR
mtd2-br.program.nameMestrado Acadêmico em Engenharia e Ciência dos Materiaispt_BR
mtd2-br.contributor.coorientadorGuerra, Nayrim Brizuela
mtd2-br.campusCampus Universitário de Caxias do Sulpt_BR
local.data.embargo2023-09-01


Arquivos deste item

Thumbnail

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples