Mostrar registro simples

dc.contributor.advisorFarias, Maria Cristina More
dc.contributor.authorPeruzzo, Marcele
dc.contributor.otherCosta, Henara
dc.contributor.otherVieceli, Alexandre
dc.contributor.otherPerottoni, Cláudio Antônio
dc.date.accessioned2018-05-23T13:19:29Z
dc.date.available2018-05-23T13:19:29Z
dc.date.issued2018-05-23
dc.date.submitted2016-02-26
dc.identifier.urihttps://repositorio.ucs.br/handle/11338/3772
dc.descriptionEste trabalho analisa o efeito da adição de boro ao aço inoxidável austenítico 316L como um aditivo da sinterização no processo de metalurgia do pó. O efeito do B foi investigado em termos da densificação, microestrutura, dureza, resistência à oxidação e ao desgaste. Os pós de 316L foram misturados com 0,6% e 0,8% em massa de boro, compactados unixialmente a 800 MPa e sinterizados em atmosfera de argônio, a uma taxa de 10°C.min-1 na temperatura de 1240°C durante 30 min. A microestrutura e as fases cristalinas das amostras sinterizadas foram avaliadas por microscopia ótica, microscopia eletrônica de varredura por emissão de campo (MEV-FEG), espectroscopia de raios X por dispersão de energia (EDS) e difração de raios X (DRX) utilizando o método de refinamento Rietveld. A técnica de calorimetria diferencial exploratória (DSC) foi realizada para estudar o comportamento das amostras de 316L com e sem adição de boro, nos estados sólido e líquido. A macrodureza das amostras sinterizadas foi medida na escala Vickers e a microdureza das fases formadas foi medida por meio de ensaios de indentação instrumentada. A composição química dos óxidos formados nas amostras de 316L com e sem adição de boro após os ensaios de oxidação cíclica nas temperaturas de 800°C, 900°C e 1000°C foram determinados por EDS e DRX. O coeficiente de atrito e o coeficiente de desgaste específico das amostras sinterizadas foram determinados por meio do ensaio de deslizamento alternado e os mecanismos de desgastes foram investigados por meio das técnicas de MEV-FEG e EDS. A adição de boro no 316L resulta em uma reação eutética entre o boro e a matriz austenítica do 316L. Os resultados de EDS e DRX revelaram a formação de dois boretos do tipo M2B ricos em Fe, Cr e Mo, (Fe,Cr)2B e (Cr,Mo)2B, provenientes da reação eutética, os quais se concentraram principalmente no contorno dos grãos austeníticos. A formação dos boretos do tipo M2B favoreceu a densificação, através da fase líquida formada durante a sinterização e promoveu o aumento da dureza, da resistência à oxidação e ao desgaste do aço inoxidável austenítico 316L.pt_BR
dc.description.abstractThis work analyses boron additions to AISI 316L austenitic stainless steels, as a sintering additive in the powder metallurgy process. The effect of boron addition was investigated in terms of densification, microstructure, hardness, oxidation resistance and wear behavior. Samples were prepared with 0.6 wt.% and 0.8 wt.% of boron, pressed to 800 MPa and sintered under argon atmosphere. Sintering cycle involved heating up to the sintering temperature of 1240°C, at a rate of 10°C.min-1, holding at this peak temperature for 30 min. Microstructure of the sintered bodies was examined by field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD), using Rietveld refinement. Differential scanning calorimetry (DSC) was used to study the behavior of both the free and boron-containing 316L samples at solid and liquid states. The Vickers hardness of sintered samples was assessed. Microhardness was evaluated using instrumented indentation. The oxide chemical composition of 316L without and containing boron samples, after cyclic oxidation at 800°C, 900°C and 100°C, was determined by EDS and XRD. The friction coefficients and specific wear coefficient of sintered samples were determined by reciprocating sliding and the wear mechanisms by FESEM and EDS. Boron addition to AISI 316L steel resulted in an eutectic reaction between the austenitic matrix and boron. EDS and XRD results revealed the formation of (Fe,Cr)2B and (Cr,Mo)2B borides, from eutectic reaction, which were concentrated mainly in intergranular sites. The formation of M2B borides favored material densification through the development of a liquid phase during sintering, and promoted an increase in hardness, oxidation and wear resistance of AISI 316L steel.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior, CAPESpt_BR
dc.language.isoptpt_BR
dc.subjectAço inoxidávelpt_BR
dc.subjectBoropt_BR
dc.subjectMetalurgia do pópt_BR
dc.subjectProcessos químicospt_BR
dc.subjectSteel, Stainlessen
dc.subjectBoronen
dc.subjectPowder metallurgyen
dc.subjectChemical processesen
dc.titleEfeito da adição de boro na microestrutura, dureza, resistência à oxidação e ao desgaste do aço inoxidável austenítico 316L sinterizado.pt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/0382010568670981pt_BR
mtd2-br.author.lattesPERUZZO, M.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação em Engenharia e Ciência dos Materiaispt_BR
mtd2-br.contributor.coorientadorBianchi, Otávio


Arquivos deste item

Thumbnail

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples