dc.descriptionO presente trabalho tem como objetivo analisar as propriedades mecânicas, térmicas, termo dinâmico-mecânicas e morfológicas de compósitos preparados com poliestireno expandido reciclado e pó de madeira. Compósitos com diferentes teores de agente compatibilizante e diferentes teores de pó de madeira foram desenvolvidos em extrusora dupla rosca co-rotante e moldados por injeção. Os resultados obtidos demonstram que o compatibilizante com maior quantidade de anidrido maleico, menor massa molar ponderal média e utilizado em quantidade igual a 2% em massa gerou compósitos com melhores propriedades mecânicas. A melhora na adesão interfacial também foi observada através da análise termo dinâmico-mecânica. Verificou-se aumento no módulo de armazenamento, redução na altura do pico de tan δ e também menor valor do fator de adesão, associado com a maior adesão na região da interface. Para os compósitos desenvolvidos com diferentes teores de pó de madeira a densidade obtida foi semelhante a densidade teórica indicando estar de acordo com a regra das misturas. A utilização de compatibilizante reduziu o teor de vazios dos compósitos. Os resultados obtidos nos ensaios de flexão demonstraram que o módulo de flexão aumenta com a quantidade de carga e também se aproxima do comportamento previsto pela regra das misturas, entretanto os compósitos sem compatibilizante apresentaram redução na resistência a flexão com o aumento do teor de pó de madeira. No ensaio de impacto observou-se redução da resistência ao impacto com a adição de carga, porém os compósitos com compatibilizante apresentaram resultados superiores aos compósitos sem compatibilizante para todos os teores de pó de madeira. Observou-se aumento no módulo de armazenamento, no módulo de perda e também na efetividade do reforço com a adição de pó de madeira. Ocorreu redução na largura e também na altura do pico de tan δ conforme a adição das partículas de madeira, contudo os compósitos com compatibilizante apresentaram redução mais acentuada devido à melhora na adesão interfacial. O modelo teórico para predizer o comportamento do módulo de armazenamento demonstrou proximidade com os valores experimentais para baixos teores de carga. Para tan δ o modelo teórico se mostrou inadequado. As micrografias dos compósitos sem compatibilizante indicaram arrancamento e a presença de vazios entre o pó de madeira e a matriz, entretanto os compósitos com compatibilizante demonstraram maior recobrimento das partículas de madeira pela matriz. A estabilidade térmica dos compósitos com compatibilizante foi reduzida para todos os teores de pó de madeira quando comparada aos compósitos sem compatibilizante.pt_BR
dc.description.abstractThe present work aims to analyze the mechanical, thermal, dynamicalmechanical thermal properties and morphology of composites based on recycled polystyrene and wood flour. Composites with different types and levels of coupling agent and also with different levels of wood flour were developed in a co-rotating twin-screw extruder and injection molded. The results show that the coupling agent with higher amount of maleic anhydride, lower weight average molecular weight and used in to 2% by weight produced composites with better mechanical properties. The improvement in interfacial adhesion was also observed by dynamical-mechanical thermal analysis. An increase in the storage modulus, decrease in peak height and also lower value of adhesion factor, was observed due to the improved on interfacial adhesion. For the composites developed with different levels of wood flour density obtained was similar to theoretical density indicating that in accordance with the rule of mixtures. The use of coupling agent reduced the concentration of voids in the composites. The flexural modulus increases with the amount of wood flour and also approaches the behavior predicted by the rule of mixtures, however the composites without coupling agent showed reduction in flexural strength. The impact strength decreases with the addition of wood flour, but the composites with coupling agent showed better results than the composite without coupling agent for all levels of wood flour. There was an increase in the storage modulus, loss modulus and also the efficiency of filler with the addition of wood flour. There was a reduction in width and also in peak height of tan δ as the addition of wood particles, composite with coupling agent demonstrated greater reduction due to improved on interfacial adhesion. The theoretical model to predict the behavior of the storage modulus showed proximity with the experimental values for low levels of filler. Theoretical model for tan δ proved inadequate. The micrographs of composites without coupling agent indicated the presence of pulled-out traces and gaps between the wood flour and matrix, however the composites with coupling agent show the strong bonding and good wetting of the fillers by the matrix. The thermal stability of composites with coupling agent was reduced for all levels of wood flour when compared to composites without coupling agent.en
dc.language.isoptpt_BR
dc.subjectPOLIMEROSpt_BR
dc.subjectPolímerospt_BR
dc.subjectPoliestirenopt_BR
dc.subjectPó de madeirapt_BR
dc.subjectMateriais - Testespt_BR
dc.subjectResistência de materiaispt_BR
dc.subjectPolymersen
dc.subjectPolystyreneen
dc.subjectWood flouren
dc.subjectMaterials - Testingen
dc.subjectStrength of materialsen
dc.titleObtenção e caracterização de compósitos preparados com poliestireno expandido reciclado e pó de madeirapt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/8723847225411507pt_BR
mtd2-br.author.lattesPOLETTO, M.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação de Mestrado em Materiaispt_BR


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record