| dc.description | Neste trabalho foi realizado um estudo para identificar a influência do ciclo de resfriamento em peças cerâmicas produzidas pelo processo de moldagem por injeção em baixa pressão. Para os testes foram produzidos dois tipos de discos utilizando uma suspensão cerâmica com 86% em peso de Alumina (Al2O3) e 14% em peso de veículo orgânico. Um disco com as dimensões de Ø80,00 x 3,00 mm foi utilizado como peça experimental para análises dimensionais (contração) e geométricas (planicidade e circularidade). Outro disco com as dimensões de Ø23,86 x 1,79 mm foi utilizado para medições de densidade e resistência à flexão pelo método biaxial de uma esfera sobre três esferas. Três condições de resfriamento foram utilizadas no molde para a fabricação dos discos cerâmicos: baixa taxa de resfriamento, alta taxa de resfriamento (ambos acionados após a injeção da suspensão cerâmica) e resfriamento contínuo durante todo o ciclo de injeção. Os resultados mostraram que a alta taxa de resfriamento obteve a maior resistência à flexão, mas com alta dispersão nos resultados. A condição com baixa taxa de resfriamento obteve maior contração dimensional, maior desvio de planicidade e menor valor de resistência à flexão, porém com menor variação. Utilizando resfriamento contínuo as amostras apresentaram uma densidade com pequena variação, porém as amostras tiveram baixa contração devido a maior compactação da suspensão cerâmica na moldagem. | pt_BR |
| dc.description.abstract | This research presents a study which has been developed to identify the influence of cooling cycle on ceramic pieces produced by the process of injection molding of ceramics in low-pressure. For the tests two types of discs using a ceramic suspension with 86 wt% of alumina (Al2O3) and 14 wt% of organic vehicle were produced. A disk with dimensions of Ø80,00 x 3,00 mm has been used as an experimental part for dimensional analysis (shrinkage) and geometric analysis (flatness and roundness). Another disc with dimensions of Ø23,86 x 1,79 mm was utilized for measuring density and flexural strength by biaxial method in a ball on three balls. Three cooling conditions were used in the mold for the manufacture of ceramic disc: low rate of cooling, high cooling rate (both initiated after injection of ceramic suspension) and continuous cooling during the injection cycle. The analyses showed that the high rate of cooling had the highest flexural strength but high dispersion in the results. The condition with low cooling rate obtained higher dimensional shrinkage, higher flatness deviation and a lower flexural strength, but with less variation. Using continuous cooling the samples showed a density with lower variation, but the samples had low shrinkage due to higher compression molding of ceramic suspension. | en |
| dc.language.iso | pt | pt_BR |
| dc.subject | Moldagem por injeção de cerâmica | pt_BR |
| dc.subject | Óxido de alumínio | pt_BR |
| dc.title | Influência do ciclo de resfriamento do molde na obtenção de discos cerâmicos por injeção em baixa pressão | pt_BR |
| dc.type | Dissertação | pt_BR |
| mtd2-br.advisor.instituation | Universidade de Caxias do Sul | pt_BR |
| mtd2-br.advisor.lattes | http://lattes.cnpq.br/7236327658667266 | pt_BR |
| mtd2-br.author.lattes | THOMAZI, E. | pt_BR |
| mtd2-br.program.name | Programa de Pós-Graduação em Engenharia Mecânica | pt_BR |
| mtd2-br.contributor.coorientador | Zorzi, Janete E. | |