Processamento reativo de nanocompósitos iPP-POSS

Abstract

The interaction modes of polyhedral oligomeric silsesquioxane (POSS) of closed cages with distinct functional groups were evaluated on isotactic polypropylene (iPP) nanostructuration via reactive processing. POSS were analyzed with isobutyl, allyl and vinyl substituent groups in concentrations of 0.5, 1, 2 and 5m% mixed with melting iPP using dicumil peroxide (DCP) as initializer. Several techniques were used to characterize the nanocomposites. The morphology was evaluated through size exclusion chromatography, Fourier transformed infrared spectroscopy, transmission electron microscopy and X-ray diffraction. The samples viscoelastic behavior in melting state was measured by oscillatory rheometry and in solid state by dynamic mechanical analysis. The thermal transitions were obtained through dynamic mechanical analysis and differential scanning calorimetry. Important morphology and viscoelastic modifications were observed in nanocomposites by dependency on the type and content of POSS used. The addition of OctaIsobutyl-POSS (OI) suggests lubricant and radicalar stabilizing action for this POSS. The AllylIsobutyl-POSS (AL) incorporation effects indicate that this one acted as plasticizing agent in function of concentration. With OctaVinyl-POSS (OV), the nanocomposites seem to acquire ramified or interlinked structure in dependency on concentration. The radicalar activation promoted by DCP was decisive in the grafting efficiency for some POSS. Therefore, the mode and the interaction intensity between nanoparticles and polymeric matrix were defined by functional groups and POSS concentration. Changes observed in morphology, thermal and viscoelastic properties as in solid state as in melting state are results of these modes and interaction degrees. It was possible to propose interaction mechanisms and morphology arrangements among iPP, DCP and POSS by evaluation of the obtained results as a whole.