| dc.description | A eletrodeposição metálica, atualmente, é uma das formas mais utilizadas para obtenção de barreiras protetivas contra meios corrosivos. Por muito tempo utilizou-se processos à base de cromo hexavalente como revestimento protetivo, porém por se tratar de um composto agressivo ao ser humano e meio ambiente, foi necessário o desenvolvimento de processos sustentáveis, como é o caso do cromo trivalente. Todavia, os revestimentos à base de cromo trivalente mostraram-se pouco eficientes quanto a proteção corrosiva, com isso necessitou-se realizar a aplicação de passivações químicas ou eletrolíticas para que houvesse um incremento no desempenho a resistência à corrosão. Dessa forma, o presente trabalho tem como principal objetivo a avaliação da melhor condição de tensão para aplicação de uma passivação trivalente eletrolítica sobre revestimento de cromo trivalente. Dentro deste contexto, decidiu-se testar, inicialmente, as condições de tensão 4, 6 e 8 volts, as quais foram baseadas na condição ideal de um processo trivalente eletrolítico já comercializado pelo fornecedor. Realizou-se um ensaio preliminar de névoa salina, selecionando as condições de tensão 4 e 6 V, as quais apresentaram melhor resultado. Realizou-se ensaios de microscopia eletrônica de varredura com emissão de campo (MEV/FEG) e espectroscopia por dispersão em energia (EDS), a fim de analisar a morfologia do filme passivante, bem como o produto de corrosão após ensaio de névoa salina. Observou-se por microscopia eletrônica de varredura (MEV/FEG) a formação de micro trincas nos corpos de provas (CP?s) passivados, em menor intensidade na condição de tensão de 4 V, também, a formação de produtos de corrosão provenientes do material base, ferro. Do mesmo modo, realizou-se ensaios eletroquímicos e de corrosão, onde foi possível observar a tendência de formação de um filme passivante e uma leve melhora na resistência a corrosão em relação ao corpo de prova sem filme passivante. Com o intuito de avaliar as possíveis alterações nas propriedades mecânicas do CP?s com filme passivante em relação ao sem camada passiva, efetuou-se ensaios de microdureza Vickers e dureza à lápis, onde não foi constatado nenhuma alteração. Contudo, no ensaio de aderência, observou-se um pequeno destacamento na condição de tensão de 4 V, porém não foi considerado significativo. As avaliações realizadas neste trabalho comprovam que a aplicação de um filme passivante pode ocasionar uma discreta melhora na resistência à corrosão. Ademais, através dos resultados obtidos pode-se concluir que mesmo obtendo uma melhora com a condição de tensão 4 V, as condições aplicadas não são as mais adequadas pois não obteve-se um filme livre de imperfeições. [resumo fornecido pelo autor] | pt_BR |
| dc.description.abstract | Currently, metallic electrodeposition is one of the most used ways to obtain protective barriers against corrosion media. For a long time, processes based on hexavalent chromium were used as a protective coating, but because it is an aggressive compound to humans and the environment, it was necessary to develop sustainable processes, such as the case of trivalent chromium. However, coatings based on trivalent chromium proved to be inefficient in terms of corrosive protection, thus it was necessary to apply chemical or electrolytic passivation so that there was an increase in corrosion resistance performance. Thus, the main objective of the present work is to evaluate the best condition for the application of a trivalent electrolytic passivation on a trivalent chromium coating. Within this context, it was decided to initially test the voltage conditions 4, 6 and 8 volts, which were based on the ideal condition of an electrolytic trivalent process already marketed by the supplier. A preliminary salt spray test was carried out, selecting the voltage conditions 4 and 6 V, which presented the best results. Scanning electron microscopy tests with field emission (SEM/FEG) and energy dispersion spectroscopy (EDS) were carried out to evaluate the morphology of the passivating film as well as the corrosion product after salt spray test. It was observed by scanning electron microscopy (SEM/FEG) the formation of micro cracks in the passivated specimens (CP's), at a lower intensity under the 4 V voltage condition, as well as the formation of corrosion products from the base material, iron. Also, electrochemical and corrosion tests were carried out, where it was possible to observe the tendency of formation of a passivating film and a slight improvement in corrosion resistance compared to the specimen without a passivating film. To evaluate the possible changes in the mechanical properties of CP's with a passive film compared to those without a passive layer, Vickers microhardness and pencil hardness tests were performed, where no changes were found. However, in the adhesion test, a small detachment was observed in the 4 V voltage condition, but it was not considered significant. The evaluations carried out in this work prove that the application of a passive film can cause an improvement in the resistance to corrosion. Furthermore, through the obtained results, it can be concluded that even with an improvement with the 4 V voltage condition, the applied conditions are not the most adequate as a film free of imperfections was not obtained. [resumo fornecido pelo autor] | pt_BR |
| dc.language.iso | pt | pt_BR |
| dc.subject | Eletrodeposição de ligas (Metalurgia) | pt_BR |
| dc.subject | Corrosão | pt_BR |
| dc.subject | Cromo | pt_BR |
| dc.subject | Engenharia química | pt_BR |
| dc.title | Desempenho à corrosão de corpos de prova de aço carbono revestidos com cromo trivalente e com posterior aplicação de um filme de passivação de cromo trivalente eletrolítico | pt_BR |
| dc.type | Monografia | pt_BR |
| mtd2-br.advisor.instituation | Universidade de Caxias do Sul | pt_BR |
| mtd2-br.program.name | Bacharelado em Engenharia Química | pt_BR |
| mtd2-br.contributor.coorientador | Catafesta, Jadna | |
| mtd2-br.campus | Campus Universitário de Caxias do Sul | pt_BR |
| local.data.embargo | 2021-06-28 | |