dc.descriptionFadiga é uma causa comum de falhas em componentes mecânicos e estruturas metálicas, quando sujeitos a carregamentos dinâmicos, causadas pelo surgimento e propagação de uma trinca de fadiga, sendo a chamada lei de Paris o principal modelo dessa propagação. Esse trabalho teve o objetivo de gerar e avaliar o processo de fadiga para o aço SAE 4140 em diferentes microestruturas, obtidas por meio da realização de tratamento térmico. As cargas dinâmicas, necessárias para a geração da fadiga nos materiais, foram obtidas mediante a utilização da vibração forçada, servindo também como controle do comprimento de trinca por meio da frequência natural, calculada previamente pelo método de elementos finitos (MEF) e verificada experimentalmente para diferentes comprimentos de trinca. Foram realizados 3 tratamentos térmicos distintos, assim como utilizados diferentes níveis de carga, para avaliação do número de ciclos e a taxa de crescimento da trinca de fadiga. Os ensaios foram feitos em corpos de prova normalizados, temperados e revenidos a 600°C e temperados e revenidos a 500°C. Com a utilização da vibração foi possível exercer dois métodos diferentes de aplicação de carga: por deslocamento e força constantes. Com carregamento por deslocamento constante foram obtidos melhores resultados quando comparado com a outra abordagem, pois na medida em que ocorreu a progressão da trinca, as tensões evoluíram com uma menor intensidade. O material temperado e revenido a 500°C teve durabilidade superior, em comparação com os demais tratamentos, independente do método de carregamento. Nos ensaios com deslocamento constante foi possível realizar o cálculo dos parâmetros m e C do modelo de Paris, obtendo-se o valor de 4,44 e 1,51 x 10-13 ( mm⁄ciclos (MPa√m) m) para m e C, respectivamente, na amostra normalizada. No material temperado e revenido a 600°C os valores foram 2,61 e 2,20 x 10-10 ( mm⁄ciclos (MPa√m) m), enquanto que na amostra temperada e revenida a 500°C foi obtido 2,50 e 2,10 x 10-10 ( mm⁄ciclos (MPa√m) m).pt_BR
dc.description.abstractFatigue is a common cause of failures in mechanical components and metal structures when subjected to dynamic loads, caused by the growth of a crack, with the so-called Paris’ law the main model for crack propagation. This work aimed to generate and evaluate the process of fatigue for the AISI 4140 steel in different microstructures, obtained by distinct heat treatments. Dynamic loads, necessary for the generation of fatigue in the material, were obtained by forced vibration, also serving as the crack length control through natural resonance frequency, previously calculated in finite elements (FEM) with experimental verification for different crack lengths. Three different heat treatments were performed, as well as different levels of loadings, to evaluate the number of cycles and the fatigue crack growth rate. Experiments were done with samples in normalized condition, quenched and tempered at 600°C and quenched and tempered at 500°C. With the use of vibration it was possible to apply two different methods of loading: constant displacement and constant force. With the displacement loading was obtained better results when compared to the other approach, since the propagation of the crack occurs, the stresses developed at a lower intensity. The quenched and tempered at 500°C sample had superior durability in comparison with the other heat treatments, regardless of the loading method. With the constant strain loading it was possible to evaluate the Paris’ law constants, m and C. For the normalized sample, the values were 4,44 e 1,51 x 10-13 (mm⁄cycles (MPa√m) m) for m and C, respectively. With the quenched and tempered at 600°C material it were obtained 2,61 e 2,20 x 10-10 ( mm⁄cycles (MPa√m) m), whereas for quenched and tempered at 500°C the results were 2,50 e 2,10 x 10-10 ( mm⁄cycles (MPa√m) m).en
dc.language.isoptpt_BR
dc.subjectAço - Fadigapt_BR
dc.subjectAço - Tratamento térmicopt_BR
dc.subjectResistência de materiaispt_BR
dc.subjectVibraçãopt_BR
dc.subjectSteel - Fatigueen
dc.subjectSteel - Heat treatmenten
dc.subjectStrength of materialsen
dc.subjectVibrationen
dc.titleCrescimento de trinca de fadiga no aço SAE 4140 sujeito à vibração forçadapt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/4156043102615068pt_BR
mtd2-br.author.lattesCAMILO, M. F.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação em Engenharia e Ciência dos Materiaispt_BR
mtd2-br.contributor.coorientadorViecelli, Alexandre


Arquivos deste item

Thumbnail

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples