dc.descriptionO constante desenvolvimento da sociedade demanda por aprimoramento em todas as áreas do conhecimento. A necessidade da utilização de concretos com elevada resistência mecânica para garantir a esbeltez de elementos construtivos ou ainda, para atender decisões arquitetônicas, muitas vezes pode comprometer o desempenho de resistência ao fogo. Nesse contexto, o trabalho avaliou o comportamento de concretos de ultra alto desempenho (CUAD) submetidos à temperatura de até 600°C. As amostras foram compostas por um teor fixo de fibras de aço carbono de 75 kg/m³ e variação do teor da adição de fibras de polipropileno em 0,0%, 0,2%, 0,6% e 1,0%, permitindo verificar a interferência das adições frente o desempenho no estado fresco, determinado pelo ensaio de mini-slump onde, com o aumento da quantidade de fibras de PP, houve significativa redução na trabalhabilidade do concreto. No estado endurecido, através dos ensaios de tração na flexão e compressão, o CUAD apresenta propriedades elevadas de resistência atreladas à própria formulação do concreto e à presença das fibras. Para o ensaio de exposição a elevadas temperaturas, as amostras foram submetidas a cura ambiente, 7 dias antes da realização do ensaio, e a cura em estufa a 60ºC, durante 48 horas antes da exposição. As amostras sem a incorporação de fibras de PP, em ambos os regimes de cura, sofreram a ocorrência do efeito spalling demonstrando que o derretimento das fibras de polipropileno, pelo efeito da elevada temperatura, diminuiu o risco de fragmentação, devido ao aumento da porosidade das amostras e, com isso, diminuição da pressão interna da matriz cimentícia. Após a exposição, as amostras com adição de 1,0% de fibras de polipropileno apresentaram melhor desempenho frente a manutenção da resistência à tração na flexão. Analisando a resistência residual à compressão, as amostras submetidas à cura em estufa, apresentaram maiores índices de resistência em função da aceleração da hidratação do cimento durante o processo de cura e de exposição à temperatura de até 600°C, conforme processo visualizado na microscopia eletrônica de varredura (MEV). [resumo fornecido pelo autor]pt_BR
dc.description.abstractThe constant development of society demands improvement in all areas of knowledge. The need to use concrete with high mechanical strength to guarantee the slenderness of constructive elements or even to meet architectural decisions can often compromise the fire resistance percentages. In this context, the work evaluated the behavior of ultra high performance concrete (UHPC) subjected to temperatures of up to 600°C. The samples were composed by a fixed content of carbon steel fibers of 75 kg/m³ and variation of the content of the addition of polypropylene fibers in 0,0%, 0,2%, 0,6% and 1,0%, allowing to verify the interference of the additions against the performance in the fresh state, determined by the mini-slump test where, with the increase of the amount of PP fibers, there was a significant reduction in the workability of the concrete. In the hardened state, through tensile tests in flexion and compression, UHPC presents high resistance properties linked to the concrete formulation and the presence of fibers. For the high temperature exposure test, the samples were subjected to room curing, 7 days before the test, and curing in an oven at 60ºC, for 48 hours before exposure. The samples without the incorporation of PP fibers, in both curing regimes, suffered the occurrence of the spalling effect, demonstrating that the melting of the polypropylene fibers, due to the effect of the high temperature, reduced the risk of fragmentation, due to the increase in the porosity of the samples and, therefore, decrease the internal pressure of the cement matrix. After exposure, samples with the addition of 1.0% of polypropylene fibers showed better performance in terms of maintaining flexural tensile strength. Analyzing the residual compressive strength, the samples submitted to oven curing showed higher resistance rates as a function of the acceleration of cement hydration during the curing process and exposure to temperatures of up to 600°C, according to the process visualized in the scanning electron microscopy (SEM). [resumo fornecido pelo autor]pt_BR
dc.language.isoptpt_BR
dc.subjectEngenharia civilpt_BR
dc.subjectConcreto de alto desempenhopt_BR
dc.subjectFibras de metalpt_BR
dc.subjectMateriais - Testespt_BR
dc.titleAnálise do desempenho mecânico de CUAD com a adição de fibras de aço carbono e de polipropileno frente exposição à elevadas temperaturaspt_BR
dc.typeMonografiapt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.program.nameBacharelado em Engenharia Civilpt_BR
mtd2-br.campusCampus Universitário de Caxias do Sulpt_BR