dc.descriptionVisando unir a sustentabilidade com o desenvolvimento econômico, é crescente a utilização de matérias-primas de fontes renováveis como alternativa para a produção de biofilmes. Os resíduos gerados no processamento da madeira correspondem à aproximadamente 50 % do seu volume inicial e sendo geralmente destinados a incineração para geração de energia, deixam de ser explorados como fonte de polissacarídeos promissores no desenvolvimento de novos materiais. Representando cerca de 20 % da composição da Mezilaurus itauba (ITA), espécie nativa do norte brasileiro utilizada amplamente no ramo madeireiro, e 24 % do Pinus elliottii (PIE), espécie amplamente cultivada no sul do Brasil utilizada em indústrias de celulose e de construção civil, a hemicelulose é um polissacarídeo amorfo estudado para aplicação desde a produção combustíveis até o desenvolvimento de filmes e géis. Nesse estudo a hemicelulose foi removida das serragens das madeiras livres de extrativos e caracterizada por FTIR e termogravimetria, onde foi constatada sua presença por meio das bandas e picos de degradação característicos das polioses. O método de extração testado não se mostrou eficiente para a remoção de hemicelulose da ITA, portanto utilizou-se apenas o conteúdo hemicelulósico extraído do Pinus em concentrações de 2 %, 3 % e 4 % (m/v), para o desenvolvimento dos filmes por casting depositados em superfície de politetrafluoretileno, que em seguida tiveram suas propriedades morfológicas, físicas, termogravimétricas e mecânicas analisadas. Os filmes apresentaram estrutura densa e sem poros com espessuras médias variando entre 0,1034 e 0,1451 mm, porém com a presença de contaminantes vistos nas microscopias e identificados como cloreto de sódio na análise EDS. Os espectros de FTIR dos filmes foram semelhantes para todas as concentrações de hemicelulose, porém a termogravimetria mostrou maior estabilidade térmica e maior teor de cinzas para o filme de 4 % (m/v). Mecanicamente, os filmes apresentaram alongamentos que variaram de 0,86 % a 2,25 %, e baixa resistência à tração possivelmente devido aos cristais de sal, dado que o filme hemicelulósico mais resistente (4 % (m/v)) suportou uma tração de 0,64 ± 0,02 MPa. Apesar da fragilidade dos filmes eles apresentaram a tendência de aumento da espessura, estabilidade térmica e resistência a tração com o aumento do teor da hemicelulose, que podem ser melhorados com o aperfeiçoamento da purificação da hemicelulose extraída. O estudo indicou a possibilidade de uso da hemicelulose extraída das madeiras de ITA e PIE para o desenvolvimento de filmes poliméricos. [resumo fornecido pelo autor]pt_BR
dc.description.abstractAiming to link sustainability to economic development, the use of raw materials from renewable sources as an alternative to the production of biofilms is growing. The residues generated in the wood processing correspond to about 50 % of its initial volume and being generally destined to incineration for energy generation, they are no longer explored as a source of polysaccharides that are promising for the development of new materials. Representing about 20 % of the composition of Mezilaurus itauba (ITA), a North Brazilian native species largely used in the timber industry, and 24 % of Pinus elliottii (PIE), a species widely cultivated in the South of Brazil used in pulp and construction industries, hemicellulose is an amorphous polysaccharide studied for application since the fuel production until the development of films and gels. In this study, hemicellulose was removed from the extractive-free wood sawdust and was characterized by FTIR and thermogravimetry, where its presence was confirmed through the IR bands and degradation peaks characteristic of the polyoses. The extraction method tested was not efficient to remove hemicellulose from ITA, therefore only the hemicellulosic content extracted from Pinus at concentrations of 2 %, 3 % and 4 % (w/v) was used to the development of films by casting placed on polytetrafluoroethylene surface, which had their morphological, physical, thermogravimetric and mechanical properties subsequently analyzed. The films exhibited a dense and pore-free structure with average thicknesses ranging from 0.1034 to 0.1451 mm, but with the presence of contaminants seen in the microscopies and identified as sodium chloride in the EDS analysis. The films' FTIR spectra were similar for all hemicellulose concentrations, but thermogravimetry showed higher thermal stability and higher ash content for the 4 % (w/v) film. Mechanically, the films presented elongations ranging from 0.86 % to 2.25 %, and low tensile strength possibly due to the salt crystals, since the most resistant hemicellulose film (4 % (w/v)) supported a tensile strength of 0.64 ± 0.02 MPa. Despite the fragility of the films, they exhibited a tendency of increasing thickness, thermal stability and tensile strength with increasing hemicellulose content, which can be improved by further purification of the extracted hemicellulose. The study indicated the possibility of utilizing hemicellulose extracted from ITA and PIE woods for the development of polymeric films. [resumo fornecido pelo autor]pt_BR
dc.language.isoptpt_BR
dc.subjectEngenharia químicapt_BR
dc.subjectHemicelulosept_BR
dc.subjectMadeirapt_BR
dc.subjectPinus elliottipt_BR
dc.subjectBiofilmespt_BR
dc.titleDesenvolvimento de filme polimérico à base de hemicelulose extraída de serragem de Mezilaurus itauba e Pinus eliottiipt_BR
dc.typeMonografiapt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.program.nameBacharelado em Engenharia Químicapt_BR
mtd2-br.campusCampus Universitário de Caxias do Sulpt_BR


Arquivos deste item

Thumbnail

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples