dc.descriptionEsta dissertação investiga a adição de embalagens flexíveis multicamadas recicladas em uma matriz de polipropileno copolímero, como um aspecto crucial para desenvolver um compósito. O objetivo principal foi o reaproveitamento deste resíduo, minimizando impactos ambientais e otimizando a disponibilidade de matéria-prima reciclada. Para alcançar esses objetivos, foi adotada uma metodologia de adição de diferentes percentuais deste resíduo através da reciclagem mecânica e incorporação por extrusão, com posterior injeção. O estudo foi dividido em duas etapas, sendo que a primeira etapa foi de inserção na matriz polimérica dos teores de 20, 30, 40, 50 e 60% do resíduo de embalagens flexíveis multicamadas. Os ensaios mecânicos demonstraram que quanto maior o percentual de resíduo no compósito, mais rígido e menos resistente ao impacto, ao passo que a densidade aumentou e o índice de fluidez reduziu. O MEV/EDS mostram que a superfície ficou bastante heterogênea. A análise de TGA mostrou que tem uma elevação do grau de degradação e no teor de cinzas residual, indicando que o resíduo e possui contaminantes inorgânicos. O DSC demonstrou uma redução no grau de cristalinidade à medida que aumenta a adição de resíduo. Já na segunda etapa, foi mantido o percentual de resíduo fixo em 50%, devido ao balanço de propriedades e para maximizar o impacto ambiental. Foi adicionado nestes compósitos, via extrusão e posterior injeção, 2,5%, 5% e 10% de agente de acoplamento Polybond 3200. As mesmas análises da primeira etapa foram realizadas e, em algumas delas, resultados otimizados foram obtidos. O índice de fluidez aumentou ao passo que a densidade ficou estabilizada. A cristalinidade voltou a aumentar, conforme foi sendo aumentada a concentração do Polybond 3200. Mas, com a adição do agente de acoplamento em concentração de 2,5% houve um acréscimo de 42,50% na resistência a flexão, ao passo que para as amostras de 5% e 10% os acréscimos foram de 33% e 34%, respectivamente. [resumo fornecido pelo autor]pt_BR
dc.description.abstractThis dissertation investigates the addition of recycled multilayer flexible packaging into a polypropylene copolymer matrix as a crucial aspect of developing a composite. The main objective was to reuse this waste, minimizing environmental impacts and optimizing the availability of recycled raw material. To achieve these goals, a methodology was adopted that involved adding different percentages of this waste through mechanical recycling and incorporation by extrusion, followed by injection molding. The study was divided into two stages, with the first stage involving the incorporation of 20%, 30%, 40%, 50%, and 60% of the multilayer flexible packaging waste into the polymer matrix. The mechanical tests showed that the higher the waste percentage in the composite, the stiffer and less impact-resistant it became, while density increased and melt flow index decreased. SEM/EDS revealed that the surface became quite heterogeneous and embedded. The TGA analysis showed an increase in the degree of degradation and residual ash content, indicating the presence of inorganic contaminants in the waste. DSC demonstrated a reduction in crystallinity as the amount of waste increased. In the second stage, the waste percentage was fixed at 50%, due to the balance of properties and to maximize environmental impact. In these composites, 2.5%, 5%, and 10% of Polybond 3200 coupling agent were added via extrusion followed by injection molding. The same analyses from the first stage were performed, and some showed optimized results. The melt flow index increased, while the density remained stable. Crystallinity increased again as the concentration of Polybond 3200 was raised. However, with the addition of 2.5% coupling agent, there was a 42.50% increase in flexural strength, while the samples with 5% and 10% showed increases of 33% and 34%, respectively. [resumo fornecido pelo autor]en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior, CAPESpt_BR
dc.language.isoenpt_BR
dc.language.isoptpt_BR
dc.subjectEmbalagens flexíveis - Reaproveitamentopt_BR
dc.subjectMateriais compostospt_BR
dc.subjectPolipropilenopt_BR
dc.subjectMateriais - Testespt_BR
dc.subjectProteção ambientalpt_BR
dc.subjectFlexible packaging - Recyclingen
dc.subjectComposite materialsen
dc.subjectPolypropyleneen
dc.subjectMaterials - Testingen
dc.subjectEnvironmental protectionen
dc.titleDesenvolvimento de compósitos de polipropileno com embalagens flexíveis recicladas moldados por injeçãopt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/1609931878679512pt_BR
mtd2-br.program.nameMestrado Acadêmico em Engenharia de Processos e Tecnologiaspt_BR
mtd2-br.campusCampus Universitário de Caxias do Sulpt_BR
local.data.embargo2024-10-01


Files in questo item

Thumbnail

Questo item appare nelle seguenti collezioni

Mostra i principali dati dell'item