dc.contributor.advisorBianchi, Otávio
dc.contributor.authorRempel, Silvana Pereira
dc.contributor.otherFrancisquetti, Edson Luiz
dc.contributor.otherAguzzoli, Cesar
dc.contributor.otherDias, Fernanda Trindade
dc.date.accessioned2018-10-01T12:49:55Z
dc.date.available2018-10-01T12:49:55Z
dc.date.issued2018-10-01
dc.date.submitted2018-07-20
dc.identifier.urihttps://repositorio.ucs.br/11338/3937
dc.descriptionEste trabalho apresenta a obtenção de micro/nanofibras de EVA utilizando o método de fiação por sopro em solução e sua possibilidade de aplicação na agricultura, no controle de pragas, através da incorporação de feromônios sexuais sintéticos. Soluções com concentração de 0,5−15% em massa de EVA em xileno: clorofórmio (96:4% em peso) foram preparadas com base no parâmetro de solubilidade do copolímero. A viscosidade das soluções, assim como o regime de concentração foi determinado por meio de medidas reológicas. A morfologia e estrutura das fibras foram avaliadas por meio de microscopia eletrônica de varredura (MEV-FEG) e difração de raios X (DRX). O perfil de liberação dos feromônios foi determinado com base na perda de massa utilizando termogravimetria (TGA). A obtenção de fibras foi possível nas soluções com regime de concentração semidiluída. As fibras apresentaram diâmetros médios de 95 a 426 nm e seus tamanhos são dependentes da taxa de alimentação. Não há evidências de que as taxas de alimentação utilizadas e a concentração tenham efeito na orientação macromolecular do EVA, assim como a utilização dos feromônios na fiação. A quantidade incorporada nas fibras, bem como a taxa de liberação dos feromônios possui influência do parâmetro de solubilidade. Portanto, dependendo da demanda de liberação é possível obter um sistema de liberação com um balanço entre taxa de liberação e tempo máximo de liberação com base na natureza do sistema polímero/solvente/feromônio.pt_BR
dc.description.abstractThis work presents the production of EVA micro/nanofibers using the solution blow spinning method and its possibility of application in agriculture, in pest control, through the incorporation of synthetic sex pheromones. Solutions with a concentration of 0.5-15% by mass of EVA in xylene: chloroform (96:4% by weight) were prepared based on the solubility parameter of the copolymer. The viscosity of the solutions as well as the concentration regime was determined by means of rheological measurements. The morphology and structure of the fibers were evaluated by means of scanning electron microscopy (SEM-FEG) and X-ray diffraction (XRD). The release profile of the pheromones was determined based on the loss of mass using thermogravimetry (TGA). Fibers were obtained in the solutions in the semi-diluted concentration regime. The fibers have diameters of 95 to 426 nm and their sizes are dependent on the feed rate. There is no evidence that feed rates used and concentration have an effect on macromolecular orientation of EVA, as well as the use of pheromones in spinning. The amount incorporated in the fibers, as well as the rate of release of the pheromones influences the solubility parameter. Therefore, depending on the release demand it is possible to obtain a release system with a balance between release rate and maximum release time based on the nature of the polymer/solvent/pheromone system.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior, CAPESpt_BR
dc.language.isoptpt_BR
dc.subjectPragas agrícolas - Controle biológicopt_BR
dc.subjectNanofibraspt_BR
dc.subjectFeromôniospt_BR
dc.subjectCiência dos materiaispt_BR
dc.subjectAgricultural pests - Biological controlen
dc.subjectNanofibersen
dc.subjectPheromonesen
dc.subjectMaterials scienceen
dc.titleObtenção de micro/nanofibras poliméricas por fiação por sopro : parâmetros e aplicação no controle de pragas agrícolaspt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/9877032679951137pt_BR
mtd2-br.author.lattesREMPEL, S. P.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação em Engenharia e Ciência dos Materiaispt_BR
mtd2-br.contributor.coorientadorCatafesta, Jadna


Files in questo item

Thumbnail

Questo item appare nelle seguenti collezioni

Mostra i principali dati dell'item