dc.descriptionO presente trabalho apresenta um estudo do efeito do hidrogênio, a influência da temperatura e do tempo no processo de pós-oxidação por plasma pulsado na liga ferrosa AISI 1045 previamente nitretada a plasma. O estudo das fases cristalinas presentes no sistema foi realizado pela técnica de difração de raios X (DRX). O método de refinamento por Rietveld foi utilizado para quantificar o conteúdo de fases presentes. A estrutura eletrônica da superfície oxidada foi estudada por espectroscopia de fotoelétron induzidos por raios X (XPS). A morfologia e espessura da camada do óxido foram avaliadas por microscopia eletrônica de varredura (MEV) e microscopia de força atômica (AFM). As propriedades mecânicas foram estudadas mediante ensaios de nanoindentação. Ensaios de névoa salina foram executados com o intuito de estudar a resistência à corrosão acelerada do sistema tratado. O hidrogênio controla a formação das fases oxidadas (hematita (α-Fe2O3) e magnetita (Fe3O4)). Uma concentração de 25% de H2 na mistura gasosa oxidante proporciona uma camada de óxido livre de hematita. Por um lado, a espessura do óxido segue um comportamento exponencial tipo Arrhenius em função da temperatura de tratamento típico de um processo termicamente induzido, com uma energia de ativação de 68±5 kJ/mol. Por outro lado, a espessura de óxido segue um comportamento tipo-parabólico com o tempo de tratamento típico de um processo de reação-difusão. Baixas temperaturas e curtos tempos de processo proporcionam camadas de óxidos mais homogêneas, compactas e com maior dureza. Os ensaios de corrosão mostraram que superfícies sem estruturas globulares, mais compactas e com poros fechados possuem uma maior resistência à corrosão, porém ainda não atende a especificação mínima para possível substituição do cromo duro em ligas ferrosas.pt_BR
dc.description.abstractThis work shows the hydrogen effect and the influence of processing temperature and time in the post-oxidation treatment by pulsed plasma on nitrided AISI 1045 ferrous alloy. The crystalline structure was analyzed by X-ray diffraction (XRD). The Rietveld refinement method was used in order to quantify the present phases in the system. The electronic structure of the oxide layer was studied by X-ray photoemission electron spectroscopy (XPS). The morphology and oxide layer thickness were analyzed by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The mechanical properties were studied by nanoindentation tests. In an effort to know the corrosion resistance of our systems, salt spray tests were executed. Hydrogen controls the formation of oxide phases (hematite (α-Fe2O3) and magnetite (Fe3O4)). A 25 % H2 concentration in the oxidation gas mixture leads to obtain a hematite-free oxide layer. On one hand, the oxide layer thickness follows an exponential Arrhenius-like behavior with processing temperature which is characteristic of a thermally induced-process with activation energy of 68±5kJ/mol. On the other hand, the oxide layer thickness follows a parabolic-like behavior with processing time which is characteristic of the reaction-diffusion process. Lower temperatures and shorter times of processing render more homogenous and compacts oxide layers with higher hardness. Although, corrosion tests show that surfaces without globular structures, more compacts and with closed-pores have higher corrosion resistances, our system does not attend the minimal specification in order to substitute hard chromium in ferrous alloys.en
dc.language.isoptpt_BR
dc.subjectEngenharia mecânicapt_BR
dc.subjectMateriais - Testespt_BR
dc.subjectNitruraçãopt_BR
dc.subjectLigas de ferropt_BR
dc.subjectCorrosão e anticorrosivospt_BR
dc.subjectMaterials testingpt_BR
dc.subjectNitridingpt_BR
dc.subjectIron alloyspt_BR
dc.subjectCorrosion and anti-corrosivespt_BR
dc.titleEfeito do hidrogênio e mecanismos na pós-oxidação por plasma pulsado de ligas ferrosas nitretadaspt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/3396179745133337pt_BR
mtd2-br.author.lattesA.C. Rovanipt_BR
mtd2-br.program.namePrograma de Pós-Graduação de Mestrado em Materiaispt_BR


Files in questo item

Thumbnail

Questo item appare nelle seguenti collezioni

Mostra i principali dati dell'item