dc.descriptionO presente trabalho apresenta um estudo do tratamento duplex para o biomaterial Nitinol (NiTi). Este tratamento consiste em nitretação a plasma para a formação do nitreto de titânio (TiN), seguido de deposição de um filme fino de nitreto de zircônio (ZrN) sobre a superfície nitretada. O estudo das fases cristalinas presentes no sistema foi realizado pela técnica de difração de raios X (DRX). A morfologia e espessura da camada nitretada e do filme fino depositado foram avaliadas por microscopia eletrônica de varredura (MEV). As propriedades mecânicas foram estudadas mediante ensaios de nanoindentação. Para avaliar a resistência à corrosão foram realizados testes de polarização potenciodinâmica em solução de saliva artificial. Os resultados mostram que a temperatura de nitretação tem forte influência na formação do TiN na superfície do substrato. O filme de ZrN depositado sobre as amostras nitretadas apresenta propriedades de dureza e resistência à corrosão que dependem da temperatura de nitretação, mesmo tendo sido depositados sem variação de temperatura. Esse comportamento sugere que os filmes são influenciados pela condição inicial da superfície antes da deposição. Os melhores resultados em termos de dureza e resistência à corrosão foram obtidos nas amostras tratadas em temperaturas mais elevadas.pt_BR
dc.description.abstractThe present work aims to study about duplex treatment on the biomaterial Nitinol (NiTi). This treatment consists in titanium nitride (TiN) formed by plasma nitration, followed by zirconium nitride (ZrN) thin film deposition upon the nitrated surface. The study of crystalline phases present in the system was performed by X-ray diffraction technique (XRD). The morphology and thickness of the nitrated layer and thin film were evaluated by scanning electron microscopy (SEM). The mechanical properties were studied by nanoindentation analysis. In order to evaluate corrosive resistance tests of potenciodynamic polarization were performed in solution of saliva artificial. Results demonstrate that nitration temperature has a strong influence in the formation TiN on the substrate surface. The ZrN film depositated upon nitrated samples present hardness and corrosive resistance properties that depend on nitration temperature, even though ZrN films were depositated without temperature variation. This behaviour suggests that films are influenced by the initial surface condition before depositon. The best results in terms of hardness and corrosive resistance were obtained in samples treated at higher temperatures.en
dc.language.isoptpt_BR
dc.subjectEngenharia de materiais e metalúrgicapt_BR
dc.subjectNitretação a plasmapt_BR
dc.subjectDeposição física de vaporpt_BR
dc.subjectMagnetron sputteringen
dc.subjectNitinolpt_BR
dc.subjectResistência de materiaispt_BR
dc.subjectTestes de durezapt_BR
dc.subjectNitreto de titâniopt_BR
dc.subjectPlasma nitridingen
dc.subjectPhysical vapor depositionpt_BR
dc.subjectMagnetron sputteringen
dc.subjectNitinolpt_BR
dc.subjectStrength of materialsen
dc.subjectHardness testsen
dc.subjectTitanium nitrideen
dc.titleSíntese e caracterização de revestimentos protetores de ZrN/TiN sobre o biomaterial Nitinol obtidos por tratamento duplex.pt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/7086202036381439pt_BR
mtd2-br.author.lattesBERNARDI, J. C.pt_BR
mtd2-br.program.namePrograma de Pós-Graduação de Mestrado em Materiaispt_BR


Ficheros en el ítem

Thumbnail

Este ítem aparece en la(s) siguiente(s) colección(ones)

Mostrar el registro sencillo del ítem