Show simple item record

dc.contributor.advisorZattera, Ademir José
dc.contributor.authorLopes, Gabriel Hoyer
dc.date.accessioned2014-06-03T18:10:51Z
dc.date.available2014-06-03T18:10:51Z
dc.date.issued2014-06-03
dc.date.submitted2010-12-10
dc.identifier.urihttps://repositorio.ucs.br/handle/11338/561
dc.descriptionNeste trabalho, foram sintetizados poliuretanos termoplásticos (TPU) via solução em reator e via extrusão reativa em extrusora dupla rosca. Os TPUs foram obtidos com o uso de pré-polímero 4,4‟-difenilmetano (MDI) e poliol poliéster, a hidroquinona bis-2-(hidróxietil)-éter (HQEE), e o n-fenilaminopropil-POSS. Os reagentes e produtos foram caracterizados através de análises de Espectroscopia no Infravermelho com Transformada de Fourier (FTIR), Calorimetria Diferencial de Varredura (DSC), análise Termogravimétrica (TGA) e reometria capilar (exclusivamente para os produtos). As análises de DSC mostraram que a presença do POSS influenciou a entalpia de fusão (ΔHm) dos TPUs sintetizados via solução. As amostras polimerizadas por extrusão reativa a 80 ºC apresentam Tm comparativamente menores que as amostras sintetizadas a 90 ºC, porém com ΔHm superior, indicando que a temperatura possivelmente favorece a formação de um número maior de cristais com um tamanho médio inferior. Também foram observados fenômenos exotérmicos durante o aquecimento das amostras sintetizadas via extrusão reativa, provavelmente devido a disponibilidade de grupos isocianato livres, detectados via FTIR, na região de ~2253 cm-1. A estabilidade térmica dos TPUs via solução também foi alterada pela adição de POSS, enquanto o polímero obtido através da extrusão reativa apresentou valores mais elevados no início da degradação. Os ensaios de TGA em isoterma apresentaram valores de perda de massa progressivamente inferiores nas amostras sintetizadas via extrusão reativa, demonstrando que tanto o POSS quanto a temperatura de síntese influem nas propriedades do polímero. Ensaios de resistência térmica nas amostras apresentaram perdas de massa inferiores nas amostras vi8a xetrusão reativa. Em ensaios de reometria capilar, a inserção do POSS levou a um aumento progressivo da viscosidade intrínseca do polímero, indicando aumento da massa molar média do TPU sintetizado via solução. Os mesmos ensaios executados com as amostras via extrusão reativa mostraram viscosidades aparentes similares, provavelmente influenciados por processos de degradação do material na célula de carga, levando a comportamentos de viscosidade sem uma tendência observável.pt_BR
dc.description.abstractIn this work, thermoplastic polyurethanes (TPU) were synthesized in solution process and reactive extrusion in twin-screw extruder. The TPUs were obtained with the use of pre-polymer based on 4,4´-Methylenediphenyl diisocyanate (MDI) and a polyester functionalized polyol, the bis-2-(hidroxyethyl)ether hidroquinone and the n-phenylaminopropyl-POSS as a second chain extender. The reagents and products were characterized using Fourier Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TGA), and also capillary rheometry (only for those products). The DSC analysis presence influenced the melting enthalpy (ΔHm) of the TPU synthesized by solution. The samples synthesized through reactive extrusion at 80 ºC presented a higher Tm compared to the 90 ºC TPUs, with a higher ΔHm, suggesting that the temperature favors the formation of a greater number of crystals with a lower medium size. Exothermic phenomena were observed during the heating of samples synthesized in reactive extrusion, probably due to the availability of free isocyanate groups, which were detected by FTIR in the ~2253 cm-1 region. The thermal stability of the TPUs was enhanced by the addition of POSS, while the polymers obtained through reactive extrusion presented higher onset degradation temperatures. The TGA analysis in isothermal conditions showed progressively lower mass loss values in samples obtained by reactive extrusion, demonstrating that the amount of POSS, as well the synthesis temperature, had influence in the final properties of the TPU. The thermal resistance of samples polymerized in reactive extrusion. In capillary rheometry tests, the insertion of POSS in the polymer led to a progressively higher value of intrinsic viscosity of the TPUs, indicating an increase in the mean molar mass of the TPUs obtained through solution synthesis. The same method was applied to the samples obtained through reactive extrusion, which showed similar apparent viscosities, yet the analysis was probably influenced by the degradation of the TPU inside the loading cell, leading to no measurable tendency in the viscosity of the polymer.en
dc.language.isoptpt_BR
dc.subjectPOLIMEROSpt_BR
dc.subjectPoliuretano termoplásticopt_BR
dc.subjectPOSSpt_BR
dc.subjectExtrusão reativapt_BR
dc.subjectPoliuretanaspt_BR
dc.subjectTermoplásticospt_BR
dc.subjectPolímerospt_BR
dc.subjectThermoplastic polyurethaneen
dc.subjectPOSSen
dc.subjectReactive extrusionen
dc.subjectPolyurethanesen
dc.subjectThermoplasticsen
dc.subjectPolymersen
dc.titleSíntese de poliuretano termoplástico modificado com POSS via extrusão reativapt_BR
dc.typeDissertaçãopt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.advisor.latteshttp://lattes.cnpq.br/6569810581342396pt_BR
mtd2-br.author.lattesLOPES, Gabriel Hoyerpt_BR
mtd2-br.program.namePrograma de Pós-Graduação de Mestrado em Materiaispt_BR


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record