Zur Kurzanzeige

dc.contributor.advisorPoletto, Matheus
dc.contributor.authorKerwald, Fernanda Borghetti
dc.contributor.otherPolidoro, Tomás
dc.contributor.otherAguzzoli, Cesar
dc.date.accessioned2021-05-31T20:10:49Z
dc.date.available2021-05-31T20:10:49Z
dc.date.issued2020-07-09
dc.date.submitted2020
dc.identifier.urihttps://repositorio.ucs.br/11338/7354
dc.descriptionOs compósitos são constituídos por dois ou mais materiais escolhidos para a formação de um material de características melhoradas, a fim de ressaltar propriedades que não podem ser vistas nos materiais quando isolados. Neste trabalho, foram desenvolvidos compósitos de polipropileno reforçados com resíduos de madeira, neste caso a madeira de itaúba. O teor de incorporação de madeira foi de 20% em massa. Como agentes de acoplamento foram testados dois óleos vegetais, o óleo de soja, óleo de soja modificado com anidrido maleico, polipropileno grafitizado com anidrido maleico, que é o agente de acoplamento comercial amplamente utilizado, no entanto, é um derivado do petróleo e desta forma, é um aditivo de fonte não renovável. O teor de adição de agente de acoplamento foi de 2% em massa. Os compósitos foram obtidos por processo de extrusão em duplarrosca e após moldados por injeção. As propriedades mecânicas, tais como resistência a tração, resistência a flexão e resistência ao impacto foram avaliadas, juntamente com a realização de análise termogravimétrica e microscopia eletrônica de varredura. Os resultados dos ensaios mecânicos mostraram que os óleos vegetais utilizados podem estar promovendo interação entre a fibra polar e matriz apolar. A adição dos óleos causou uma redução na resistência a flexão de aproximadamente 8%, quando comparada a amostra sem agente de acoplamento. A adição dos óleos acarretou em um aumento de 10% da resistência ao impacto dos compósitos, quando comparada a amostra sem tratamento. O uso do agente de acoplamento de fonte não renovável melhorou a resistência a tração e também a flexão, em virtude da melhor adesão causada por esse aditivo. Contudo, o uso do polipropileno grafitizado com anidrido maleico deixou o material mais rígido e reduziu a resistência ao impacto dos compósitos. A análise termogravimétrica mostrou que o uso dos óleos não resultou na redução da estabilidade térmica dos compósitos, quando comparada a amostra sem tratamento, o que pode indicar a melhora na adesão fibra matriz. Por outro lado, o uso do agente de acoplamento comercial reduziu a estabilidade térmica do compósito. Os resultados deste trabalho indicam que a adição de agentes de acoplamento de origem vegetal como o óleo de soja podem ser uma alternativa viável a utilização de compósitos provenientes de fontes não renováveis, como o petróleo. [resumo fornecido pelo autor]pt_BR
dc.description.abstractComposites are formed by two or even more materials chosen to form a new material with improved characteristics, in order to highlight certain characteristics that are not able to be observed when those materials are seen separately. In this work, it was developed polypropylene composites reinforced with wood waste, to say wood from Itaúba. The wood incorporation content was 20% by weight. As coupling agents, it was tested a couple of vegetable oils, such as soybean oil and soya oil modified with maleic anhydride, polypropylene graphitized with maleic anhydride, which is the commercial coupling agent widely used. This agent is a derivative of petroleum and, by being so, it is an additive of non-renewable source. The coupling agent addition content was 2% by mass. The composites were obtained by double-screw extrusion and after they were molding by injection. The mechanical properties, such as tensile strength, flexural strength and impact strength, were evaluated along with thermogravimetric analysis and scanning electron microscopy. The results of the mechanical tests showed that the vegetable oils used may be promoting interaction between the polar fiber and the non-polar matrix. The addition of oils caused a reduction in flexural strength of approximately 8%, when compared to the sample without coupling agent. The addition of the oils resulted in a 10% increase in the impact resistance of the composites, when compared to the sample without treatment. The usage of the non-renewable source coupling agent improved the tensile strength and also the flexion, due to the better adhesion caused by this additive. However, the use of polypropylene graphitized with maleic anhydride made the material more rigid and reduced the impact resistance of the composites. The thermogravimetric analysis showed that the use of oils did not result in a reduction in the thermal stability of the composites, when compared to the sample without treatment, which may indicate the improvement in the fiber adhesion. On the other hand, the use of the commercial coupling agent reduced the thermal stability of the composite. The results indicate that the addition of coupling agents of plant origin such as soybean oil can be a viable alternative to the use of composites from non-renewable sources, such as petroleum. [resumo fornecido pelo autor]en
dc.language.isoptpt_BR
dc.subjectPolipropilenopt_BR
dc.subjectMadeirapt_BR
dc.subjectÓleo de sojapt_BR
dc.titleAvaliação do uso de agente compatibilizante de fonte renovável em compósitos de polipropileno e resíduos de madeirapt_BR
dc.typeMonografiapt_BR
mtd2-br.advisor.instituationUniversidade de Caxias do Sulpt_BR
mtd2-br.program.nameEngenharia Química - Bachareladopt_BR
mtd2-br.contributor.coorientadorJonko, Eliena
mtd2-br.campusCampus Universitário de Caxias do Sulpt_BR
local.data.embargo2020-07-09 00:00:00